PVC 200 foam core

PVC foam offers optimal stiffness-to-weight-ratio, good impact strength , water resistance, thermal insulation, low resin absorption and high fatigue resistance. PVC foam is also self extinguishing therefore it has good fire performances. It is compatible with polyester, viniliester and epoxy resin. PVC foam is easy to work it can be rolled, cut etc..

PVC foam can be applied in different sectors: marine ( decks, bulkheads, interiors, hulls,etc..), public vehicles (floors, interiors, partition walls, roof panels, front ends), wind energy (rotor blades, turbine generator housings), sports ( skis, snowboard, kayaks etc..) and so on.

 

DOWNLOAD PDF

Request for Quotation

PVC 200 foam core
Application areas Automotive

 

TECHNICAL FEATURES

Density kg/m3
ASTM D1622
kg/m³
nominal
200
Compressive strength
ASTM D1621-10
MPa
average min-ave
min-min
4,84
4,64
4,00
Compressive modulus
ASTM D1621-10
MPa
average min-ave
min-min
212
198
172
Tensile strength
ASTM D1623
MPa
average min-ave
min-min
6,61
5,61
5,33
Tensile modulus
ASTM D1623
MPa
average min-ave
min-min
415
343
317
Shear strength
ASTM C273
MPa
average min-ave
min-min
3,59
3,23
2,81
Shear modulus
ASTM C273
MPa
average min-ave
min-min
78
74
65
Shear elongation at break
ASTM C273
%
average
41
Standard block dimensions
 
mm
 
750
1600
48
Disclaimer

LIABILITY DISCLAIMER: The above data are to the best of our knowledge correct and are intended to give information about our products and their potential applications. No warranty is given or implied in respect of certain properties of the products or their suitability for a particular application. We reserve the right for technical changes without further notice. We guarantee impeccable product quality under our terms of sale.