PVC foam offers optimal stiffness-to-weight-ratio, good impact strength , water resistance, thermal insulation, low resin absorption and high fatigue resistance. PVC foam is also self extinguishing therefore it has good fire performances. It is compatible with polyester, viniliester and epoxy resin. PVC foam is easy to work it can be rolled, cut etc..

PVC foam can be applied in different sectors: marine ( decks, bulkheads, interiors, hulls,etc..), public vehicles (floors, interiors, partition walls, roof panels, front ends), wind energy (rotor blades, turbine generator housings), sports ( skis, snowboard, kayaks etc..) and so on.

 

 

DOWNLOAD PDF

Request for Quotation

 

TECHNICAL FEATURES

Density kg/m3
ASTM D1622
kg/m³
nominal
130
Compressive strength
ASTM D1621-10
MPa
average min-ave
min-min
2,73
2,52
2,25
Compressive modulus
ASTM D1621-10
MPa
average min-ave
min-min
125
111
99
Tensile strength
ASTM D1623
MPa
average min-ave
min-min
3,81
3,04
2,79
Tensile modulus
ASTM D1623
MPa
average min-ave
min-min
216
185
170
Shear strength
ASTM C273
MPa
average min-ave
min-min
2,03
1,97
1,79
Shear modulus
ASTM C273
MPa
average min-ave
min-min
49
45
41
Shear elongation at break
ASTM C273
%
average
32
Standard block dimensions
 
mm
 
850
1900
58
Disclaimer

LIABILITY DISCLAIMER: The above data are to the best of our knowledge correct and are intended to give information about our products and their potential applications. No warranty is given or implied in respect of certain properties of the products or their suitability for a particular application. We reserve the right for technical changes without further notice. We guarantee impeccable product quality under our terms of sale.